Fracture Assessment of Weld Joints of High-Strength Steel in Pre-Strained Condition

Abstract

Unstable fractures tend to occur after ductile crack initiation or propagation. In most collapsed steel structures, a maximum 15% pre-strain was recorded, at the steel structural connections, during the great earthquake of 1995, in Japan. Almost-unstable fractures were observed in the beam-to-column connections, where geometrical discontinuities existed. Structural collapse and unstable failure occurred after large-scale plastic deformations. Ship structures can also suffer from unstable fractures in the welded joints. The fracture resistance of butt-welded joints subjected to tension in the pre-strained condition was estimated by considering the toughness deterioration, due to pre-strain and toughness correction for constraint loss in a tension specimen. The target specimen for this fracture assessment was a double-edged, through-thickness crack panel, with a crack in the weld joint (heat-affected zone (HAZ)). The critical fracture toughness value (crack tip opening displacement (CTOD)) of a large structure with pre-strain, which was applied to the HAZ region, was estimated from a small-scale, pre-stained, three-point bend specimen. Fracture toughness values, evaluated by a CTOD test, were recently mandated for shipbuilding steel plates. The critical fracture toughness value is a very useful parameter to evaluate the safety of huge ship structures.