Effect of Vanadium Content on the Microstructure and Mechanical Properties of IN718 Alloy by Laser Cladding

Abstract

Microalloying vanadium can change the segregation state of Nb element in IN718 alloy, reduce the formation of harmful Laves phase and refine the dendritic structure of IN718 alloy during the laser process. Therefore, IN718 alloys with V content from 0.081 to 1.88 wt.% were prepared and evaluated. Metallographic microscopy and scanning electron microscopy were used to observe the corresponding morphology, structure, and distribution of elements. First of all, it was found that the addition of V refines the grain size of IN718 alloy and reduces the primary dendrite arm spacing. Secondly, adding V to IN718 alloy can reduce the porosity of the cladding layer. The elements are uniformly distributed in the cladding layer, and the addition of vanadium reduces the segregation degree of the Nb element, which is conducive to homogenization. In addition, microhardness and residual stress were also investigated. Finally, the addition of vanadium was shown to have no apparent effect on the tensile strength and yield strength but can significantly improve the elongation of IN718 alloy. In conclusion, the microstructure and mechanical properties of IN718 alloy with 0.081 wt.% vanadium content provide a new solution to improve the application level of IN718 alloy in laser cladding.