Relationship Between Matrix Cracking and Delamination in CFRP Cross-Ply Laminates Subjected to Low Velocity Impact

Author:

Tan Riming,Xu Jifeng,Sun Wei,Liu ZhunORCID,Guan Zhidong,Guo Xia

Abstract

The effect of matrix cracking on the delamination morphology inside carbon fiber reinforced plastics (CFRP) laminates during low-velocity impact (LVI) is an open question. In this paper, the relationship between matrix cracking and delamination is studied by using cross-ply laminates. Several methods, including micrograph, C-scan, and visual inspection, were adopted to characterize the damage after LVI experiments. Based on the experimental results, finite element (FE) models were established to analyze the damage mechanisms. The matrix cracking was predicted by the extended finite element method (XFEM) and the Puck criteria, while the delamination was modeled by cohesive elements. It was revealed that the matrix crack in the bottom ply not only promoted the outward propagation of delamination but also contributed to the narrow delamination beneath the impact location. Multiple matrix cracks occurred in the middle ply. The ones close to the plate center initiated the delamination and prevented large-scale delamination beneath the impact location. For the cracks that were far away, no significant effect on delamination was found. In conclusion, the stress redistribution caused by the crack opening determines the delamination.

Publisher

MDPI AG

Subject

General Materials Science

Cited by 14 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3