Abstract
Ni-Cr-Mo alloy coatings with different content of Cr element were produced on carbon structural steel by laser cladding. Coatings exhibited similar phase composition containing γ-Ni solid solution and similar microstructure composed of primary grains and eutectics with segregated Mo. Corrosion behavior of coatings in a sulfuric acid dew point corrosion environment were investigated through the combination of immersion test, electrochemical measurements, and surface analysis. Coatings exhibited similar passive behavior and passive film with a bilayer structure consisting of a compact inner layer and a porous outer layer. An increase in Cr resulted in a more protective passive film with thicker and more compacting inner layer. However, the corrosion resistance was firstly degraded as the content of Cr increased from 18 wt.% to 22 wt.%, and then improved as the content of Cr increased from 22 wt.% to 26 wt.%. This phenomenon was attributed to the competition effect between the increase in Cr and relative decrease in Ni.
Funder
Fundamental Research Funds for the Central Universities
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献