Abstract
WSiN films were produced through hybrid pulse direct current/radio frequency magnetron co-sputtering and evaluated as diffusion barriers for Cu metallization. The Cu/WSiN/Si assemblies were annealed for 1 h in a vacuum at 500–900 °C. The structural stability and diffusion barrier performance of the WSiN films were explored through X-ray diffraction, Auger electron spectroscopy, and sheet resistance measurement. The results indicated that the Si content of WSiN films increased from 0 to 9 at.% as the power applied to the Si target was increased from 0 to 150 W. The as-deposited W76N24, W68Si0N32, and W63Si4N33 films formed a face-centered cubic W2N phase, whereas the as-deposited W59Si9N32 film was near-amorphous. The lattice constants of crystalline WSiN films decreased after annealing. The sheet resistance of crystalline WSiN films exhibited a sharp increase as they were annealed at 800 °C, accompanied by the formation of a Cu3Si compound. The failure of the near-amorphous W59Si9N32 barrier against Cu diffusion was observed when annealed at 900 °C.
Funder
Ministry of Science and Technology, Taiwan
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献