The Effects of Graphene on the Biocompatibility of a 3D-Printed Porous Titanium Alloy

Author:

Sun Xu,Tong Shuang,Yang Shude,Guo Shu

Abstract

3D-printed titanium (Ti) materials have attracted much attention in the field of bone tissue repair. However, the combination strength of traditional alloy materials with bone tissue is lower, and the elastic modulus is higher than that of natural bone tissue, which makes the titanium alloy susceptible to stress shielding phenomena after implantation. Therefore, it is urgent to find better surface modification technology. In this study, the physical and chemical properties, toxicity, and proliferation of adipose stem cells of composite graphene-coated titanium alloy (Gr–Ti) were investigated using 3D-printed titanium alloy as a material model. Physical and chemical property tests confirmed that 3D printing could produce porous titanium alloy materials; the compressive strength and elastic modulus of the titanium alloy scaffolds were 91 ± 3 MPa and 3.1 ± 0.4 GPa, matching the elastic modulus of normal bone tissue. The surface characterization shows that graphene can be coated on titanium alloy by a micro-arc oxidation process, which significantly improves the surface roughness of titanium alloy. The roughness factor (Ra) of the Ti stent was 4.95 ± 1.12 μm, while the Ra of the Gr–Ti stent was 6.37 ± 0.72 μm. After the adipose stem cells were co-cultured with the scaffold for 4 h and 24 h, it was found that the Gr–Ti scaffold could better promote the early cell adhesion. CCK-8 tests showed that the number of ADSCs on the G–Ti scaffold was significantly higher than that on the Ti scaffold (p < 0.01). The relative growth rate (RGR) of ADSCs in Gr–Ti was grade 0–1 (non-toxic). In the in vivo experiment of repairing a critical bone defect of a rabbit mandible, the bone volume fraction in the Gr–Ti group increased to 49.42 ± 3.28%, which was much higher than that in the Ti group (39.76 ± 3.62%) (p < 0.05). In conclusion, the porous graphene–titanium alloy promotes the proliferation and adhesion of adipose stem cells with multidirectional differentiation potential, which has great potential for the application of bone tissue engineering in repairing bone defects in the future.

Funder

the National Natural Science Foundation of China

the China Postdoctoral Science Foundation

Publisher

MDPI AG

Subject

Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3