Gao Longxin,Lai Yong,Islam Pramanic Mohammad Rashadul,Zhang Wuman
Abstract
The deterioration of Portland cement pervious concrete (PCPC) subjected to wet-dry cycles in the simulated acid rain solution was investigated; 4% silica fume (SF) and 8% fine aggregate (FAG) were used to replace part of cement and the coarse aggregates (weight by weight), respectively. The wear resistance, the compressive, and flexural strength of PCPC were measured. The results show that after 12 wet-dry cycles in acid rain solution the compressive strength and the flexural strength of control PCPC are decreased by 30.7% and 40.8%. The final compressive strength of PCPC with 4% SF and PCPC with 8% FAG is increased by 6.9% and 30.3%, and the final flexural strength is increased by 25.4% and 72.3%, respectively. The wear loss of PCPC is decreased by 58.8% and 81.9% when 4% SF and 8% FAG is added to PCPC, respectively. The microstructures of PCPC with wet-dry cycles are also discussed.
Funder
National Natural Science Foundation of China
Subject
General Materials Science
Reference67 articles.
1. Pervious concrete: A sustainable drainage solution;Bassuoni;Concrete,2010
2. Cyclic Heat Island Impacts on Traditional versus Pervious Concrete Pavement Systems
3. Hot weather comparative heat balances in pervious concrete and impervious concrete pavement systems;Kevern;J. Heat Isl. Inst. Int.,2012
4. Influence of aggregate size and gradation on acoustic absorption of enhanced porosity concrete;Marolf;ACI Mater. J.,2004
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献