Evaluation of Tensile Bond Strength between Self-Adhesive Resin Cement and Surface-Pretreated Zirconia

Abstract

The tensile bond strength between zirconia subjected to different surface-pretreatment methods and methacryloyloxydecyl-dihydrogen-phosphate (MDP)-containing self-adhesive resin cement was evaluated herein. Eighty-eight cylindrical zirconia specimens were randomly divided into the following four groups based on the pretreatment method: (1) no treatment, (2) air abrasion, (3) HNO3/HF etching, and (4) zirconia-nanoparticle coating. The tensile bond strength of the zirconia–resin-cement complexes was investigated. One-way ANOVA and post hoc tests were performed at a 95% significance level, and the Weibull modulus was calculated. Fracture patterns were visualized by SEM. The surface roughness of the specimens without resin bonding was evaluated by AFM. The tensile bond strength of the specimens decreased as follows: Groups 3 > 4 > 2 > 1 (28.2 ± 6.6, 26.1 ± 5.7, 16.6 ± 3.3, and 13.9 ± 3.0 MPa, respectively). Groups 3 and 4 had significantly higher tensile bond strengths (p < 0.05) and lower fracture probabilities than those of Groups 1 and 2. They also showed both mixed failure and resin-cement cohesive failure, whereas Groups 1 and 2 showed mixed failure exclusively. The zirconia–resin tensile bond was stronger after HNO3/HF etching or ZrO2-nanoparticle coating than after air abrasion or no treatment. The estimated surface roughness decreased as follows: Groups 3 > 4 > 2 > 1. The combination of zirconia pretreated with HNO3/HF etching or ZrO2-nanoparticle coating and an MDP-containing self-adhesive resin cement can increase the clinical longevity of zirconia restorations by preventing their decementation.