Abstract
Chromium (III) oxide is a technologically interesting material with attractive chemical, catalytic, magnetic and mechanical properties. It can be produced by different chemical and physical methods, for instance, by metal–organic chemical vapor deposition, thermal decomposition of chromium nitrate Cr(NO3)3 or ammonium dichromate (NH4)2Cr2O7, magnetron sputtering and atomic layer deposition. The latter method was used in the current work to deposit Cr2O3 thin films with thicknesses from 28 to 400 nm at deposition temperatures from 330 to 465 °C. The phase composition, crystallite size, hardness and modulus of elasticity were measured. The deposited Cr2O3 thin films had different structures from X-ray amorphous to crystalline α-Cr2O3 (eskolaite) structures. The averaged hardness of the films on SiO2 glass substrate varied from 12 to 22 GPa and the moduli were in the range of 76–180 GPa, as determined by nanoindentation. Lower values included some influence from a softer deposition substrate. The results indicate that Cr2O3 could be a promising material as a mechanically protective thin film applicable, for instance, in micro-electromechanical devices.
Funder
European Regional Developemment Fund
European Regional Development Fund
Subject
General Materials Science,General Chemical Engineering
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献