Effect of Secondary Phase on Electroless Ni Plating Behaviour of Super Duplex Stainless Steel SAF2507 for Advanced Li-Ion Battery Case

Abstract

The development of Li-ion battery cases requires superior electrical conductivity, strength, and corrosion resistance for both cathode and anode to enhance safety and performance. Among the various battery case materials, super duplex stainless steel (SDSS), which is composed of austenite and ferrite as two-phase stainless steel, exhibits outstanding strength and corrosion resistance. However, stainless steel, which is an iron-based material, tends to have lower electrical conductivity. Nevertheless, nickel-plating SDSS can achieve excellent electrical conductivity, making it suitable for Li-ion battery cases. Therefore, this study analysed the plating behaviour of SDSS plates after nickel plating to leverage their exceptional strength and corrosion resistance. Electroless Ni plating was performed to analyse the plating behaviour, and the plating behaviour was studied with reference to different plating durations. Heat treatment was conducted at 1000 °C for one hour, followed by cooling at 50 °C/s. Post-heat treatment, the analysis of phases was executed using FE-SEM, EDS, and EPMA. Electroless Ni plating was performed at 60–300 s. The plating duration after the heat treatment was up to 300 s, and the behaviour of the materials was observed using FE-SEM. The phase analysis concerning different plating durations was conducted using XRD. Post-heat treatment, the precipitated secondary phases in SAF2507 were identified as Sigma, Chi, and CrN, approximating a 13% distribution. During the electroless Ni plating, the secondary phase exhibited a plating rate equivalent to that of ferrite, entirely plating at around 180 s. Further increments in plating time displayed growth of the plating layer from the austenite direction towards the ferrite, accompanied by a reduced influence from the substrate. Despite the differences in composition, both the secondary phase and austenite demonstrated comparable plating rates, showing that electroless Ni plating on SDSS was primarily influenced by the substrate, a finding which was primarily confirmed through phase analysis.