Abstract
In order to investigate the effect of graphene nanoribbons on the final properties of hydroxyapatite-based nanocomposites, a solvothermal method was used at 180 °C and 5 h for the synthesis of graphene nanoribbons–hydroxyapatite nanopowders by employing hydrogen gas injection. Calcium nitrate tetrahydrate and diammonium hydrogenphosphate were used as calcium and phosphate precursors, respectively. To synthesize the powders, a solvent containing diethylene glycol, anhydrous ethanol, dimethylformamide, and water was used. Graphene oxide nanoribbons were synthesized by chemical unzipping of carbon nanotubes under oxidative conditions. The synthesized powders were consolidated by spark plasma sintering methodat 950 °C and a pressure of 50 MPa. The powders and sintered samples were then evaluated using X-ray diffraction, Raman spectroscopy, high-resolution transmission electron microscopy, Vickers microindentation techniques, and biocompatibility assay. The findings of this study showed that the final powders synthesized by the solvothermal method had calcium to phosphate ratio of about 1.67. By adding a small amount of graphene nanoribbon (0.5%W), elastic modulus and hardness of hydroxyapatite increased dramatically. In biological experiments, the difference of hydroxyapatite effect in comparison with the nanocomposite was not significant. The findings of this study showed that graphene nanoribbons have a positive effect on the properties of hydroxyapatite, and these findings would be useful for the medical and theranostic application of this type of nanocomposites.