Author:
Zhao Xu,Qi Yuhong,Wang Jintao,Zhang Zhanping,Zhu Jing,Quan Linlin,He Dachuan
Abstract
To study the effect of cast defects on the corrosion behavior and mechanism of the UNS C95810 alloy in seawater, an investigation was conducted by weight loss determination, scanning electron microscopy (SEM), confocal laser scanning microscopy (CLSM), X-ray diffraction (XRD) and electrochemical testing of the specimen with and without cast defects on the surface. The results show that the corrosion rate of the alloy with cast defects is higher than that of the alloy without cast defects, but the defects do not change the composition of the resulting corrosion products. The defects increase the complexity of the alloy microstructure and the tendency toward galvanic corrosion, which reduce the corrosion potential from −3.83 to −86.31 mV and increase the corrosion current density from 0.228 to 0.23 μA⋅cm−2.