Interdiffusion and Intermetallic Compounds at Al/Cu Interfaces in Al-50vol.%Cu Composite Prepared by Solid-State Sintering

Abstract

Al–Cu composites have attracted significant interest recently owing to their lightweight nature and remarkable thermal properties. Understanding the interdiffusion mechanism at the numerous Al/Cu interfaces is crucial to obtain Al–Cu composites with high thermal conductivities. The present study systematically investigates the interdiffusion mechanism at Al/Cu interfaces in relation to the process temperature. Al-50vol.%Cu composite powder, where Cu particles were encapsulated in a matrix of irregular Al particles, was prepared and then sintered at various temperatures from 340 to 500 °C. Intermetallic compounds (ICs) such as CuAl2 and Cu9Al4 were formed at the Al/Cu interfaces during sintering. Microstructural analysis showed that the thickness of the interdiffusion layer, which comprised the CuAl2 and Cu9Al4 ICs, drastically increased above 400 °C. The Vickers hardness of the Al-50vol.%Cu composite sintered at 380 °C was 79 HV, which was 1.5 times that of the value estimated by the rule of mixtures. A high thermal conductivity of 150 W∙m−1∙K−1 was simultaneously obtained. This result suggests that the Al-50vol.%Cu composite material with large number of Al/Cu interfaces, as well as good mechanical strength and heat conductance, can be prepared by solid-state sintering at a low temperature.