Abstract
The aim of this study was to compare three different light-curing-units (LCUs) and determine their effectiveness in the adhesive cementation of indirect composite restorations when a light-curing resin cement is used. Two resin composites were selected: Enamel Plus HRI (Micerium) and AURA (SDI). Three thicknesses (3 mm, 4 mm and 5 mm) were produced and applied as overlays and underlays for each resin composite. A standardized composite layer was placed between underlay and overlay surfaces. Light curing of the resin-based luting composites was attained through the overlay filters using LCUs for different exposure times. All specimens were allocated to experimental groups according to the overlay thickness, curing unit and curing time. Vickers Hardness (VH) notches were carried out on each specimen. Data were statistically evaluated. The curing unit, curing time and overlay thickness were significant factors capable of influencing VH values. The results showed significantly decreased VH values with increasing specimen thickness (p < 0.05). Significant differences in VH values were found amongst the LCUs for the various exposure times (p < 0.05). According to the results, a time of cure shorter than 80 s (with a conventional quartz–tungsten–halogen LCU) or shorter than 40 s (with a high-power light-emitting diode (LED) LCU) is not recommended. The only subgroup achieving clinically acceptable VH values after a short 20 s curing time included the 3 mm-thick overlays made out of the AURA composite, when the high-power LED LCU unit was used (VH 51.0). Composite thickness has an intense effect on polymerization. In clinical practice, light-cured resin cements may result in insufficient polymerization for high thickness and inadequate times. High-intensity curing lights can attain the sufficient polymerization of resin cements through overlays in a significantly shorter time than conventional halogen light.
Subject
General Materials Science
Reference43 articles.
1. Self-adhesive resin cements: A literature review;Radovic;J. Adhes. Dent.,2008
2. Influence of curing time, overlay material and thickness on three light-curing composites used for luting indirect composite restorations;D’Arcangelo;J. Adhes. Dent.,2012
3. Luting of CAD/CAM ceramic inlays: Direct composite versus dual-cure luting cement
4. Effect of Repeated Preheating Cycles on Flexural Strength of Resin Composites
5. Influence of a Repeated Preheating Procedure on Mechanical Properties of Three Resin Composites
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献