Abstract
Bulk nanocrystalline materials of small and medium ferromagnetic content were produced using severe plastic deformation by high-pressure torsion at room temperature. Giant magnetoresistive behavior was found for as-deformed materials, which was further improved by adjusting the microstructure with thermal treatments. The adequate range of annealing temperatures was assessed with in-situ synchrotron diffraction measurements. Thermally treated Cu–Co materials show larger giant magnetoresistance after annealing for 1 h at 300 °C, while for Cu-Fe this annealing temperature is too high and decreases the magnetoresistive properties. The improvement of magnetoresistivity by thermal treatments is discussed with respect to the microstructural evolution as observed by electron microscopy and ex-situ synchrotron diffraction measurements.
Funder
H2020 European Research Council
Subject
Fluid Flow and Transfer Processes,Computer Science Applications,Process Chemistry and Technology,General Engineering,Instrumentation,General Materials Science
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献