The Influence of the Second Phase on the Microstructure Evolution of the Welding Heat-Affected Zone of Q690 Steel with High Heat Input

Abstract

Q690 steel is widely used as building steel due to its excellent performance. In this paper, the microstructure evolution of the heat-affected zone of Q690 steel under simulated high heat input welding conditions was investigated. The results show that under the heat input of 150–300 kJ/cm, the microstructures of the heat-affected zone are lath bainite and granular bainite. The content of lath bainite gradually decreased with the increase in heat input, while the content of granular bainite steadily increased. The proportion of large-angle grain boundaries decreased from 51.1% to 40.3%. Overall, the average size of original austenite increased, and the precipitates changed from Ti (C, N) to Cr carbides. During the cooling process, the nucleation position of bainitic ferrite was from high to low according to the nucleation temperature, and in order of inclusions at grain boundaries, triple junctions, intragranular inclusions, bainitic ferrite/austenite phase boundaries, twin boundaries, grain boundaries, and intragranular inclusions at the bainitic ferrite/austenite phase interface. The growth rate of bainitic ferrite nucleated at the phase interface, grain boundary, and other plane defects was faster, while it was slow at the inclusions. Moreover, it was noted that the Mg-Al-Ti-O composite inclusions promote the nucleation of lath bainitic ferrite, while the Al-Ca-O inclusions do not facilitate the nucleation of bainitic ferrite.