Synthesis and Processing of Melt Spun Materials from Esterified Lignin with Lactic Acid

Abstract

In this study, the carbon fiber manufacturing process is investigated, using high-density polyethylene (HDPE) and esterified lignin either with lactic acid (LA) or with poly(lactic acid) (PLA) as precursors. More specifically, lignin was modified using either LA or PLA in order to increase its chemical affinity with HDPE. The modified compounds were continuously melt spun to fibrous materials by blending with HDPE in order to fabricate a carbon fiber precursor. The obtained products were characterized with respect to their morphology, as well as their structure and chemical composition. Moreover, an assessment of both physical and structural transformations after modification of lignin with LA and PLA was performed in order to evaluate the spinning ability of the composite fibers, as well as the thermal processing to carbon fibers. This bottom–up approach seems to be able to provide a viable route considering large scale production in order to transform lignin in value-added product. Tensile tests revealed that the chemical lignin modification allowed an enhancement in its spinning ability due to its compatibility improvement with the commercial low-cost and thermoplastic HDPE polymer. Finally, stabilization and carbonization thermal processing was performed in order to obtain carbon fibers.