Abstract
In this work, the preparation of magneto-plasmonic granular nanostructures and their evaluation as efficient substrates for magnetically assisted surface enhanced Raman spectroscopy (SERS) sensing are discussed. These nanostructures consist of star-shaped gold Au shell grown on iron oxide Fe3-xO4 multicores. They were prepared by seed-mediated growth of anisotropic, in shape gold nanosatellites attached to the surface of polyol-made iron oxide polycrystals. In practice, the 180 nm-sized spherical iron oxide particles were functionalized by (3-aminopropyl) triethoxysilane (APTES) to become positively charged and to interact, in solution, with negatively charged 2 nm-sized Au single crystals, leading to nanohybrids. These hybrids acted subsequently as nucleation platforms for the growth of a branched gold shell, when they were contacted to a fresh HAuCl4 gold salt aqueous solution, in the presence of hydroquinone, a reducing agent, for an optimized nominal weight ratio between both the starting hybrids and the gold salt. As expected, the resulting nanocomposites exhibit a high saturation magnetization at room temperature and a rough enough plasmonic surface, making them easily attracted by a lab. magnet, while exhibiting a great number of SERS hot spots. Preliminary SERS detection assays were successfully performed on diluted aqueous thiram solution (10−8 M), using these engineered substrates, highlighting their capability to be used as chemical trace sensors.
Funder
Graduate University of Science and Technology
Subject
General Materials Science,General Chemical Engineering
Cited by
17 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献