Author:
Huang Lijie,Han Xiaoxue,Chen Haobin,An Shuxiang,Zhao Hanyu,Xu Hao,Huang Chongxing,Wang Shuangfei,Liu Yang
Abstract
In this study, we investigated the barrier properties of a montmorillonite-reinforced biomass material, starch. Organically modified montmorillonite materials were prepared from natural montmorillonite by reacting it with dodecyl trimethyl ammonium chloride, dodecyl dimethyl benzyl ammonium chloride or octadecyl trimethyl ammonium chloride under ultrasonic conditions. The composite starch films incorporated with these organically modified montmorillonite samples were characterized by scanning electron microscopy, transmission electron microscopy, infrared spectroscopy and X-ray diffraction. The results showed that the introduction of montmorillonite decreases the transmittance of the composite film by 10% in the visible region and significantly inhibits UV-light transmittance. The decomposition temperature of the composite film ranges from 200 to 500 °C, with a weight loss rate of 80%. The distance between the montmorillonite layers increases from 0.14 nm in the non-magnetized state to 1.49 nm after magnetization. The oxygen permeability of the starch film modified by organic montmorillonite (0.067 cm3/m2·d) is lower than that of the montmorillonite starch film without magnetization (0.097cm3/m2·d). The oxygen barrier capacity is close to zero. Particularly in the ordered magnetic montmorillonite starch composite film, the oxygen barrier ability is the best. Therefore, modified montmorillonite could serve as an excellent reinforcing agent for cassava starch films and effectively improve the oxygen barrier performance of the films.
Funder
Guangxi Science and Technology project
National College Students' innovation and entrepreneurship training program
Subject
Polymers and Plastics,General Chemistry
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献