Abstract
Foam insulation materials are widely used in the construction industry due to their low thermal conductivity attributable to their microstructures and their low-conductivity blowing agents and affordability. In this study, we evaluate how the thermal performance of foam insulation materials used for the exterior walls of buildings, viz., extruded polystyrene (XPS), polyisocyanurate (PIR), and phenolic foam (PF), age over the life cycle of a building. To compare the aging of thermal performance during the life cycle of a building, each material was tested at 70 and 110 °C and with slicing acceleration according to EN and ISO standards. The thermal conductivity of each foam insulation material was measured using a heat flow meter at an operating temperature of 23 °C and converted into thermal resistance values. Different foam insulation materials have different aging procedures according to material-specific EN standards, while ISO 11561 applies the same procedure to all material classifications. Upon comparing the aged values according to ISO and EN standards to the initial values, the analysis showed a change rate of 23 to 26% in PIR and 18 to 20% in PF. In XPS, a rate of change of 10 to 23.8% was calculated. Our results indicated that the slicing acceleration induced a thermal resistance reduction rate about three times faster than aging at 70 °C. However, the long-term changed thermal resistance values of the foam insulation material applied via the calculating procedure specified in the ISO and EN standards were similar.
Funder
Technology Innovation Program
Ministry of Trade, Industry and Energy
Subject
Polymers and Plastics,General Chemistry
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献