We report the effect of the curing (Tcuring) and annealing (Tanneal) temperatures on the structural, electrical, and optical properties of solution processed tin oxide. Tanneal was varied from 300 to 500 °C, and Tcuring from 200 °C to Tanneal. All Tanneal lead to a polycrystalline phase, but the amorphous phase was observed at Tanneal = 300 °C and Tcuring ranging from 250 to 300 °C. This could be explained by the melting point of the precursor (SnCl2), occurring at 250 °C. The crystallinity can be effectively controlled by the annealing temperature, but the curing temperature dramatically affects the grain size. We can reach grain sizes from 5–10 nm (Tcuring = 200 °C and Tanneal = 300 °C) to 30–50 nm (Tcuring = 500 °C and Tanneal = 500 °C). At a fixed Tanneal, Hall mobilities, carrier concentration, and conductivity increased with the curing temperature. The Hall mobility was in the range of 1 to 9.4 cm2/Vs, the carrier concentration was 1018 to 1019 cm−3, and the conductivity could reach ~20 S/cm when the grain size was 30–50 nm. The optical transmittance, the optical bandgap, the refractive index, and the extinction coefficient were also analyzed and they show a correlation with the annealing process.
Funder
Ministry of Trade, Industry and Energy
Subject
Inorganic Chemistry,Condensed Matter Physics,General Materials Science,General Chemical Engineering
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献