Author:
Wang Yifeng,Feng Guangjie,Wei Yan,Hu Bingxu,Deng Dean
Abstract
In this paper, the SiCp/Al composites were bonded via laser-induced exothermic reactions of a Ni–Al–Zr interlayer. The Ni–Al–Zr interlayer was designed based on its exothermic property and chemical compatibility with the SiCp/Al composites. The influences of the interlayer composition and bonding pressure on the joint microstructure and shear strength were investigated. Results indicated that high exothermic reactions occurred in the Ni–Al–Zr interlayer and realized the reliable bonding with the SiCp/Al composites. The interlayer products were the eutectic structure of NiAl+Ni2AlZr+Ni3Al5Zr2. NiAl3 and Ni2Al3 reaction layers were formed at the bonding interfaces. The interlayer composition and the bonding pressure determined the morphology and distribution of the voids and the reaction layers, thus controlling the joint shear strength. When the SiCp/Al composites were bonded using the interlayer with the Zr content of 15 wt.% under the bonding pressure of 3 MPa, the joint shear strength reached the maximum of 24 MPa.
Funder
National Natural Science Foundation of China
Natural Science Foundation of Chongqing
Fundamental Research Funds for the Central Universities
Subject
Inorganic Chemistry,Condensed Matter Physics,General Materials Science,General Chemical Engineering
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献