Abstract
Membrane water content is of vital importance to the freezing durability of proton exchange membrane fuel cells (PEMFCs). Excessive water freezing could cause irreversible degradation to the cell components and deteriorate the cell performance and lifetime. However, there are few studies on the critical membrane water content, a threshold beyond which freezing damage occurs, for cold storage of PEMFCs. In this work, we first proposed a method for measuring membrane water content using membrane resistance extracted from measured high frequency resistance (HFR) based on the finding that the non-membrane resistance part of the measured HFR is constant within the range of membrane water content of 2.98 to 14.0. Then, freeze/thaw cycles were performed from −50 °C to 30 °C with well controlled membrane water content. After 30 cycles, cells with a membrane water content of 8.2 and 7.7 exhibited no performance degradation, while those higher than 8.2 showed significant performance decay. Electrochemical tests revealed that electrochemical surface area (ECSA) reduction and charge transfer resistance increase are the main reasons for the degradation. These results indicate that the critical membrane water content for successful cold storage at −50 °C is 8.2.
Funder
National Key Research and Development Program of China
Science and Technology Support Project of State Grid Corporation of China
Subject
Energy (miscellaneous),Energy Engineering and Power Technology,Renewable Energy, Sustainability and the Environment,Electrical and Electronic Engineering,Control and Optimization,Engineering (miscellaneous)
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献