Sliding Layer Formation during Tribological Contact between Expanded Graphite and Stainless Steel—A Pilot Study

Author:

Rewolińska Aleksandra1,Leksycki Kamil2ORCID,Perz Karolina1,Kinal Grzegorz1ORCID

Affiliation:

1. Faculty of Civil and Transport Engineering, Poznan University of Technology, Piotrowo Street, 60-965 Poznan, Poland

2. Institute of Mechanical Engineering, University of Zielona Gora, 4 Prof. Z. Szafrana Street, 65-516 Zielona Gora, Poland

Abstract

The sliding layer created during operation of the expanded graphite–steel combination has had a huge impact on the effectiveness of the friction process, and thus on the sustainable development of society. Knowledge of the factors determining the properties of the sliding layer will make it possible to reduce friction resistance in the future through the proper design and selection of sliding pairs for given applications. This paper studies the effect of the moisture content of expanded graphite on the formation of a sliding layer on a stainless steel surface. The tests were carried out in static contact for 30 s and dynamic contact for 15 and 30 min, for loads of 10, 20, and 30 N and speeds of 25 and 50 mm/s. To determine the changes in surface geometry due to material transfer, the Ra roughness value of the surface of stainless steel samples was measured. In order to realize the purpose of the work and evaluate the effect of moist rings on the resulting sliding layer, the results of the surface roughness of stainless steel samples working with dry and moist graphite rings were compiled. The obtained results show that the presence of water in the stainless steel-expanded graphite friction node affects the formation of a sliding layer. The resulting layer reduces the surface roughness of the cooperating materials and prevents their accelerated wear. After 5 min of work with the water-soaked graphite counter-sample, depending on the applied friction conditions, a reduction in the surface roughness of the stainless steel sample was achieved in the range of 11–18% compared to the initial value. After 30 min of operation, the surface roughness decreased by 3 to 25%. Pilot studies have shown that operating conditions influence the formation of a sliding layer in the stainless steel-expanded graphite tribological contact. This confirms the validity of conducting further research in this area.

Publisher

MDPI AG

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3