Preparation and Dispersion Performance of Hydrophobic Fumed Silica Aqueous Dispersion
Author:
Xu Jinglu1, Wang Jihu1ORCID, Wen Shaoguo1, Ding Shengnan1, Song Jia1, Jiang Sihong1, Wang Haopeng1
Affiliation:
1. College of Chemistry and Chemical Engineering, Shanghai University of Engineering Science, Shanghai 201620, China
Abstract
Hydrophobic fumed silica (HFS) is a commonly used rheology additive in waterborne coatings. A series of experiments were conducted on the HFS-dispersing technology in this study. The size and structure of HFS primary particles were observed via transmission electron microscopy (TEM). The measurement results of the TEM were D50 = 13.6 nm and D90 = 19.7 nm, respectively. The particle size and dispersion performance of HFS were tested via dynamic light scattering (DLS). Additionally, the HFS aqueous dispersion was prepared and compounded with waterborne polyacrylic latex and polyurethane resin. The elemental distribution of the coatings was characterized using energy dispersive spectroscopy (EDS). The results show that the HFS in a non-ionic polymer dispersant had the best dispersion performance. The particle size of the HFS in the aqueous dispersion is related to the dispersion conditions. Under optimized conditions, the HFS aqueous dispersion can be prepared with a particle size of D50 = 27.2 nm. The HFS aqueous dispersion has stable storage stability. Even after storage for 47 d, the particle size still did not change significantly.
Subject
Polymers and Plastics,General Chemistry
Reference41 articles.
1. Correlation between process and silica dispersion/distribution into composite: Impact on mechanical properties and Weibull statistical analysis;Siot;Polym. Test.,2018 2. Li, J., Niu, G., Bai, W., Ma, Y., Xiong, Q., Qin, C., Zhang, J., An, R., and Ren, W. (2021). Significant Improvement of Anticorrosion Properties of Zinc-Containing Coating Using Sodium Polystyrene Sulfonate Noncovalent Modified Graphene Dispersions. Coatings, 10. 3. Development of single layer nanoparticle anti-reflection coating for polymer substrates;Moghal;Thin Solid Film.,2013 4. Xie, J., Zhang, H., Shao, Y., Bao, D., Zhang, H., and Zhu, J. (2020). Investigation of the Performance of Fumed Silica as Flow Additive in Polyester Powder Coatings. Coatings, 10. 5. Di, Z., Ma, S., Wang, H., Guan, Z., Lian, B., Qiu, Y., and Jiang, Y. (2022). Modulation of Thermal Insulation and Mechanical Property of Silica Aerogel Thermal Insulation Coatings. Coatings, 12.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献
|
|