Effect of Welding Peak Temperature on Microstructure and Impact Toughness of Heat-Affected Zone of Q690 High Strength Bridge Steel

Abstract

The effect of peak temperature (TP) on the microstructure and impact toughness of the welding heat-affected zone (HAZ) of Q690 high-strength bridge steel was studied using a Gleeble-3500 thermal simulation testing machine. The results show that the microstructure of the inter critical heat-affected zone (ICHAZ) was ferrite and bainite. The microstructure of fine grain heat-affected zone (FGHAZ) and coarse grain heat-affected zone (CGHAZ) was lath bainite (LB), lath martensite (LM), and granular bainite (GB), but the microstructure of FGHAZ was finer. With the increase in peak temperature, the content of LB and GB decreased, the content of LM increased, and the lath bundles of LM and LB gradually became coarser. With the increase in peak temperature, the grain size of the original austenite increased significantly, and the impact toughness decreased significantly. When the peak temperature was 800 °C, the toughness was the best. For CGHAZ, the peak temperature should be less than 1200 °C to avoid excessive growth of grain and reduction of mechanical property.