Effects of Sand Powder on Sulfuric Acid Resistance, Compressive Strength, Cost Benefits, and CO2 Reduction of High CaO Fly Ash Concrete

Abstract

This article studies the efficiency of sand powder as a supplementary cementitious material (SCM) in improving the sulfuric acid resistance of concrete incorporated with high CaO fly ash. Besides, the effects of sand powder on compressive strength development, mitigation of carbon dioxide emission, and cost-effectiveness are addressed. Paste mixtures with W/B ratios of 0.25 and 0.40 were used in this study for the performances of sulfuric acid resistance and long-term compressive strength development. The test results indicated that sand powder could reduce the weight loss of the tested paste specimens in sulfuric acid solution with a pH of 1, compared to the control specimens, especially for the specimens incorporated with high CaO fly ash. The sand powder addition could also increase the compressive strength of cement pastes at the age of 90 days by 26.27% and 43.80% for W/B ratios of 0.25 and 0.40, respectively. The use of sand powder in the evaluated concrete mixture could also reduce CO2 emission by 23.23% and lower the cost of the mixtures by 8.05%, compared to the control mixture. The addition of sand powder could significantly increase the sulfuric acid resistance, compressive strength, and economic benefits and reduce the CO2 emission of high CaO fly ash-cement-based materials.