Effect of Growth Temperature on Structural Quality of In-Rich InxAl1−xN Alloys on Si (111) Substrate by RF-MOMBE

Abstract

In-rich InAlN films were grown directly on Si (111) substrate by RF-MOMBE without any buffer layer. InAlN films were grown at various substrate temperatures in the range of 460–540°C with TMIn/TMAl ~3.3. Structural properties of InAlN ternary alloys were investigated with X-ray diffraction, scanning electron microscopy, and transmission electron microscopy (TEM). It is shown that the deposited In0.8AlM0.2N (0001) films can be in epitaxy with Si (111) substrate with orientation relationship of [2̅110]InAlN//[11̅0]Si. Also, the growth rate around ~0.25 μm/h almost remains constant for growth in the temperature range from 460 to 520°C. Cross-sectional TEM from InAlN grown on Si (111) at 460°C shows that the epitaxial film is in direct contact with Si without any interlayer.