Abstract
AbstractThanks to its advantages of high efficiency and near‐net shaping, laser directed energy deposition (LDED) is rapidly becoming a remarkable preparation technology for high‐purity ceramics. However, the cracking problem in shaping process is always a great challenge for LDED to achieve industrial application. For this purpose, alumina/aluminum titanate melt‐growth ceramics (A/AT MGCs) were prepared using LDED system, and the corresponding finite element thermal analysis model was developed. The solidification behavior and cracking mechanism of A/AT MGCs were investigated based on the thermal analysis model, and the influence of process parameters on the cracking characteristics was revealed with experiments. Results show that the crack morphology and distribution are controlled by microstructure and temperature gradient together. The scanning speed of 100–150 mm/min, with better microstructure and lower temperature gradient, is a preferred process window. This study provides theoretical guidance and technical support for the cracking suppression during LDED shaping of ceramics.
Funder
National Natural Science Foundation of China
Fundamental Research Funds for the Central Universities
Subject
Materials Chemistry,Ceramics and Composites
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献