Characterization of initial intergranular oxidation processes in alloy 600 at a sub-nanometer scale-Reference-Cited by-同舟云学术

Characterization of initial intergranular oxidation processes in alloy 600 at a sub-nanometer scale

Published:2018-04 Issue: Volume:133 Page:36-47
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Persaud S.Y.,Langelier B.,Korinek A.,Ramamurthy S.,Botton G.A.,Newman R.C.

Funder

Nuclear Ontario, an ORF-RE network and the Natural Sciences and Engineering Research Council of Canada

University Network of Excellence in Nuclear Engineering

Canada Foundation

McMaster University

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference59 articles.

1. The influence of dissolved hydrogen on nickel alloy SCC: a window to fundamental insight;Morton,2001

2. In search of the true temperature and stress intensity factor dependencies for PWSCC;Morton,2005

3. Primary Water SCC Understanding and Characterization Through Fundamental Testing in the Vicinity of the Nickel/Nickel Oxide Phase Transition;Morton,2002

4. Effects of Hydrogen on Stress Corrosion Crack Growth Rate of Nickel Alloys in High-Temperature Water

5. Effect of dissolved hydrogen on SCC of Ni alloys and weld metals;Andresen,2009

Cited by 31 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Hydrogen embrittlement and strain rate sensitivity of electrodeposited copper: part I – the effect of hydrogen content;npj Materials Degradation;2024-08-05

2. Effect of fretting wear regimes on stress corrosion cracking of Alloy 690TT in high-temperature pressurized water;Corrosion Science;2024-08

3. Influence of dissolved hydrogen and IG Cr carbide on the oxidation behavior of Alloy 600 in hydrogenated primary water;Nuclear Engineering and Technology;2024-08

4. Evading the intermediate-temperature embrittlement of L12-strengthened high entropy alloys by alleviating intergranular oxidation;Corrosion Science;2024-04

5. Intergranular corrosion of Ni-30Cr in high-temperature hydrogenated water after removing surface passivating film;npj Materials Degradation;2024-03-13