Arc Characteristics and Welding Process of Magnetic Field Assisting Plasma-GMAW-P

Author:

YU JIANG, ,ZHANG HONGTAO,HE PENG,YANG XIAO,TENG YAO,WANG QICHEN,WEI LIQIN,ZHANG WENJIE

Abstract

Low-carbon steel Q235B was successfully joined by plasma-pulsed gas metal arc welding (plasma-GMAW-P) with an external magnetic field. The arc profile, temperature field, electrical signal, microstructure, and mechanical properties of this method were analyzed. The results indicated that the coupling degree of the two arcs increased with the strengthening of the magnetic field current. However, when the magnetic field current was greater than 1 A, the arc pro-file changed slightly with the increase of the magnetic field current. Fixed on the magnetic field current, the coupling degree first increased and then decreased with the increase of the plasma welding current, GMAW-P welding current, plasma gas flow rate, and nozzle height, respectively. The maximum temperature had no obvious influence on joint penetration at different magnetic field cur-rents. However, the average temperature had an inverse effect on joint penetration at different magnetic field currents. The weld fusion zone joint tensile test results showed that the ratio of depth to width increased with the application of magnetic field currents. Moreover, tensile strength on the upper and lower part of the tensile samples were 521 and 488 MPa, respectively, which were 4.6% and 3.2% higher than those without the magnetic field. The microhardness of the weld joints was higher than that without the magnetic field.

Publisher

American Welding Society

Subject

Metals and Alloys,Mechanical Engineering,Mechanics of Materials

Cited by 8 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3