Abstract
The paper presents tribological tests of selected materials used as liners in a composite hydraulic cylinder. Three coating materials were used for the analysis: Sika F180 polyurethane, Huntsman Araldite LY1564 with Aradur 3487 amine hardener and Bezlona 1111 Super Metal. In addition, uncoated carbon epoxy laminate (CFRP) samples were used as reference material. The instantaneous course of the friction force, its maximum and average value, were the analysed parameters. Ball-on-disk tests were performed on a specialised tester that allows, among other things, to control the operating conditions (clamping force, operating temperature, speed, friction path) and measurement of the instantaneous value of the friction force. After these tests, the friction paths were observed using a Leica DCM8 contactless profilometer with an EPI 20x lens. The amount of energy dissipated due to friction was also determined. The conducted tests and comparative analyses allowed to conclude that the F180 material is the most desirable in terms of tribological properties.
Publisher
Vilnius Gediminas Technical University
Reference21 articles.
1. Aerospace Technology Institute. (2017). INSIGHT_09 - Composite materials - september 2018. Cranfield.
2. ASTM International. (2018). Standard test method for wear testing with a pin-on-disk apparatus (ASTM Standard G99-17). https://www.astm.org/g0099-17.html
3. Structural Health Monitoring Technology for Aerospace Composite Propellant Tank
4. Limit load evaluation of hydraulic actuators
5. Static and Flexural Fatigue Behavior of GFRP Pultruded Rebars
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献