High-entropy alloys: Structure, mechanical properties, deformation mechanisms and application

Abstract

The article considers a brief review of the foreign publications on the study of the structure, phase composition and properties of five-component high-entropy alloys (HEAs) in different structural states in a wide temperature range over the past two decades. HEAs attract the attention of scientists with their unique and unusual properties. The difficulties of comparative analysis and generalization of data are noted due to different methods of obtaining HEAs, modes of mechanical tests for uniaxial compression and tension, sizes and shapes of the samples, types of thermal treatments, and phase composition (bcc and fcc crystal lattices). It is noted that the HEA with a bcc lattice has mainly high strength and low plasticity, and the HEA  with a fcc lattice has low strength and increased plasticity. A significant increase in the properties of the FeMnCoCrNi HEA with a fcc lattice can be achieved by alloying with boron and optimizing the parameters of thermal mechanical treatment at alloying with carbon in the amount of 1 % (at.). The deformation curves analyzed in the temperature range –196 ÷ 800 °C indicate an increase in the yield strength with a decrease in the grain size from 150 to 5 microns. As the temperature decreases, the yield strength and elongation increase. The effect of deformation rate on the mechanical properties is an increase in the ultimate strength and yield strength, which is most noticeable at high rates of 10–2 ÷ 103 s–1. The features of HEAs deformation behavior in the mono- and poly-crystalline states are noted. The complex of high operational properties of HEAs makes it possible to use them in various industries. There are good prospects of using energy treatment to modify the surface layers and further improve HEAs properties.