Wear Evaluation of Prosthetic Materials Opposing Themselves

Abstract

SUMMARY The purpose of the present in vitro study was to compare the two-body wear resistance of a type 3 gold alloy (Aurocast8), two lithium disilicate glass ceramics (IPS e.max CAD and IPS e.max Press), a heat-pressed feldspathic porcelain (Cerabien ZR Press), an yttria-stabilized tetragonal zirconia polycrystal ceramic (Katana Zirconia ML), and three heat-cured composite resins (Ceram.X Universal, Enamel Plus Function, and Enamel Plus HRi) opposing antagonistic cusps made out of the same restorative materials. Ten 6-mm-thick samples and 10 cusp-shaped abraders were manufactured with each test material (n=10) according to standard laboratory procedures. All sample/antagonist pairs made out of the same material were subjected to a two-body wear test in a dual-axis chewing simulator for up to 120,000 loading cycles. The total vertical wear (mm) and the total volumetric loss (mm3) for each sample/antagonist pair were calculated. Data were statistically analyzed using one-way analysis of variance tests. The total vertical wear for the gold alloy was not significantly different compared to Ceram.X Universal, Enamel Plus Function, IPS e.max CAD, and Cerabien ZR Press. Significantly increased wear values were observed for Enamel Plus HRi and IPS e.max Press. The lowest values for total vertical wear and volumetric loss were recorded on the monolithic zirconia.