WEAR RESISTANCE OF ELECTRODEPOSITED Fe-W ALLOY COATINGS UNDER DRY CONDITIONS AND IN THE PRESENCE OF RAPESEED OIL-Reference-Cited by-同舟云学术

WEAR RESISTANCE OF ELECTRODEPOSITED Fe-W ALLOY COATINGS UNDER DRY CONDITIONS AND IN THE PRESENCE OF RAPESEED OIL

Published:2018-03-28 Issue:1 Volume:1 Page:16-23
ISSN:2351-521X
Container-title:Green Tribology
language:
Short-container-title:

Author:

Nicolenco A.¹,Tsyntsaru N.¹,Matijošius T.²,Asadauskas S.²,Cesiulis H.¹

Affiliation:

1. Physical Chemistry Department, Vilnius University, Vilnius, Lithuania

2. Institute of Chemistry, Center for Physical Sciences and Technology, Vilnius, Lithuania

Abstract

Amorphous Fe-W alloys with 25 at.% of W were electrodeposited under direct and pulse modes from glycolate-citrate bath with and without addition of polyethylene glycol. The tribological behavior of the coatings was studied at 1, 2 and 5 N loads under dry friction and in the presence of rapeseed oil films of 0.2-5.0 m thickness. The tribological behavior of obtained coatings at dry friction reveals their severe tribo-oxidation resulting in a high wear depth and coefficient of friction. Observed groove like surface with well-adhered particles inside the wear track point out on abrasive-adhesive wear mechanism of Fe-W alloys. In the presence of rapeseed oil films the wear mechanism changes, and values of coefficient of friction decrease up to 10 times compared to dry friction conditions. The optimum thickness of rapeseed oil film was 1 μm. This film has the satisfactory adhesion and uniform distribution on the surface, and could withstand up to 2 000 cycles.

Publisher

Vytautas Magnus University

Reference20 articles.

1. Micromechanical and tribological properties of nanocrystalline coatings of iron-tungsten alloys electrodeposited from citrate-ammonia solutions

2. Corrosion behaviour of electrodeposited nanocrystalline Ni–W and Ni–Fe–W alloys

3. Tribological and corrosive characteristics of electrochemical coatings based on cobalt and iron superalloys

4. Iron–tungsten alloys electrodeposited under direct current from citrate–ammonia plating baths

5. Evaluating Electrocatalysts for the Hydrogen Evolution Reaction Using Bipolar Electrode Arrays: Bi- and Trimetallic Combinations of Co, Fe, Ni, Mo, and W

Cited by 4 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. The Influence of Sodium Tungstate Concentration on the Electrode Reactions at Iron–Tungsten Alloy Electrodeposition;Coatings;2021-08-18

2. Green Tribology;Tribology in Materials and Manufacturing - Wear, Friction and Lubrication;2021-02-03

3. Nanocrystalline Electrodeposited Fe-W/Al2O3 Composites: Effect of Alumina Sub-microparticles on the Mechanical, Tribological, and Corrosion Properties;Frontiers in Chemistry;2019-04-16

4. Improvement in the Wear Resistance under Dry Friction of Electrodeposited Fe-W Coatings through Heat Treatments;Coatings;2019-01-24