Structural, optical, and mechanical properties of TiO2 nanolaminates

Author:

Ghazaryan LilitORCID,Handa Shiti,Schmitt PaulORCID,Beladiya VivekORCID,Roddatis Vladimir,Tünnermann Andreas,Szeghalmi AdrianaORCID

Abstract

Abstract The structural, optical, and mechanical properties of TiO2 nanolaminate films grown by plasma-enhanced atomic layer deposition are discussed. Several TiO2/Al2O3 and TiO2/SiO2 compositions have been investigated to study the effect of the relative number of ALD oxide cycles on the film properties to obtain a high refractive index coating with low optical losses, low roughness, and low mechanical stress. The formation of crystalline TiO2 observed at high deposition temperature, or film thickness was inhibited by periodically introducing ultra-thin amorphous layers into the film. Only 4 ALD cycles of Al2O3 (corresponding to ca. 0.5 nm) between 335 ALD cycles of TiO2 (ca. 11 nm) form a closed, distinct layer suppressing the crystallization in TiO2 film. Consequently, the roughness of the pure TiO2 film is reduced from ca. 20 nm rms to 1 nm rms in the 335/4 nanolaminate, with only a slight decrease of the refractive index from 2.46 to 2.44 in 100 nm pure TiO2 and the nanolaminate, respectively. The refractive indices of the nanolaminates in various compositions vary between 2.38 and 2.50 at 632 nm, and the corresponding optical losses from the films are low. The mechanical stress was reduced to about 140 MPa in several TiO2/Al2O3 nanolaminates; however, lower mechanical stress has not been obtained with the studied compositions. The nanolaminate structure is preserved up to 600 °C annealing temperature. After annealing at 800 °C, the individual layers interdiffuse into each other so that no distinct nanolaminate structure is detected. By using TiO2/Al2O3 nanolaminates with reduced mechanical stress, a narrow bandpass filter was realized on various substrates, including half-ball and aspherical lenses.

Funder

Fraunhofer IOF Center of Excellence in Photonics

Deutsche Forschungsgemeinschaft

Fraunhofer Society

Publisher

IOP Publishing

Subject

Electrical and Electronic Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science,General Chemistry,Bioengineering

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3