Plasma enhanced atomic layer deposition of silicon nitride using magnetized very high frequency plasma

Author:

Ji You Jin,Kim Hae In,Kang Ji Eun,Choi Seung Yup,Kim Ki Hyun,Kim Doo SanORCID,Ellingboe A R,Kim Hye Min,Yeom Geun YoungORCID,Kim Dong Woo

Abstract

Abstract To obtain high-quality SiN x films applicable to an extensive range of processes, such as gate spacers in fin field-effect transistors (FinFETs), the self-aligned quadruple patterning process, etc, a study of plasma with higher plasma density and lower plasma damage is crucial in addition to study on novel precursors for SiN x plasma-enhanced atomic layer deposition (PEALD) processes. In this study, a novel magnetized PEALD process was developed for depositing high-quality SiN x films using di(isopropylamino)silane (DIPAS) and magnetized N2 plasma at a low substrate temperature of 200 °C. The properties of the deposited SiN x films were analyzed and compared with those obtained by the PEALD process using a non-magnetized N2 plasma source under the same conditions. The PEALD SiN x film, produced using an external magnetic field (ranging from 0 to 100 G) during the plasma exposure step, exhibited a higher growth rate (∼1 Å/cycle) due to the increased plasma density. Additionally, it showed lower surface roughness, higher film density, and enhanced wet etch resistance compared to films deposited using the PEALD process with non-magnetized plasmas. This improvement can be attributed to the higher ion flux and lower ion energy of the magnetized plasma. The electrical characteristics, such as interface trap density and breakdown voltage, were also enhanced when the magnetized plasma was used for the PEALD process. Furthermore, when SiN x films were deposited on high-aspect-ratio (30:1) trench patterns using the magnetized PEALD process, an improved step coverage of over 98% was achieved, in contrast to the conformality of SiN x deposited using non-magnetized plasma. This enhancement is possibly a result of deeper radical penetration enabled by the magnetized plasma.

Publisher

IOP Publishing

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3