Xu Yan,Bi Liuhan,Liu Yinglai,Xu Tianhan,Feng Zhenjun,Bai Qiang,Yang Fengping
Abstract
Abstract
Duplex stainless steel has been widely applied to industry. In this paper, nondestructive testing, chemical composition analysis, metallographic analysis, hardness test, and scanning electron microscope were used to study the causes of the crack in the butt joint girth weld of pipe and flange. Both steel pipe and flange are duplex stainless steel S31803. Through analysis, it was judged that the crack was a crystalline crack, generated in the welding process, which was related to the welding process and the control of the welding installation gap between the steel pipe and the flange with unequal wall thickness.
Subject
General Physics and Astronomy
Reference9 articles.
1. Study on the effect of hot working parameters on deformation resistance of duplex stainless steel;Qi,2021
2. Weld forming and microstructure characteristics of 2205 duplex stainless steel via an assisted magnetic field;Sun;Transactions of the China Welding Institution.,2022
3. Finite Element Modelling of Cutting Forces in Face Milling of Duplex Stainless Steel 2205;Sambedana;NFEST 2019. Kurukshetra,2019
4. Effect of sulfur, phosphorus, silicon, and delta ferrite on weld solidification cracking of AISI 310S austenitic stainless steel;Almomani;Engineering Failure Analysis,2022
5. Nondestructive techniques for the detection of sigma phase in duplex stainless steel: a comprehensive review[J];Biezma;Engineering Failure Analysis,2021