Size effect and electrical ageing of PDMS dielectric elastomer with competing failure modes

Abstract

Abstract Large-scale dielectric elastomer generators dielectric elastomer generators (DEGs) such as those employed in wave energy converter projects require a significant volume of electrically stressed materials. Meanwhile, predictions of energy output from such systems are generally extrapolated from electrical and mechanical breakdown measurements performed on small scale samples, where the presence of small defects can be extremely small. This can lead to overly optimistic upscaled predictions for the performance and reliability of full-scale devices. In this study, multilayer DEGs were prepared to evaluate the dielectric breakdown strength of thin polydimethylsiloxane PDMS elastomer at different values of active areas. The results indicated the presence of two separate breakdown mechanisms resulting in an enhanced size effect and a reduced reliability for the larger samples. Electrical ageing tests were performed on three different sample geometries and the dielectric breakdown strength was found to be marginally affected by the time under stress. A Weibull competing failure model was applied to the distribution of experimental breakdowns and electrical reliability was accurately modeled over more than four decades of variation in the electrode area.