Author:
Jones Jason B.,Wimpenny David I.,Gibbons Greg J
Abstract
Purpose
– This paper aims to investigate the effects on material properties of layer-by-layer application of pressure during fabrication of polymeric parts by additive manufacturing (AM). Although AM, also known popularly as 3D printing, has set a new standard for ease of use and minimal restraint on geometric complexity, the mechanical part properties do not generally compare with conventional manufacturing processes. Contrary to other types of polymer processing, AM systems do not normally use (in-process) pressure during part consolidation.
Design/methodology/approach
– Tensile specimens were produced in Somos 201 using conventional laser sintering (LS) and selective laser printing (SLP) – a process under development in the UK, which incorporates the use of pressure to assist layer consolidation.
Findings
– Mechanical testing demonstrated the potential to additively manufacture parts with significantly improved microstructure and mechanical properties which match or exceed conventional processing. For example, the average elongation at break and ultimate tensile strength of a conventionally laser-sintered thermoplastic elastomer (Somos 201) increased from 136 ± 28 per cent and 4.9 ± 0.4 MPa, to 513 ± 35 per cent and 10.4 ± 0.4 MPa, respectively, when each layer was fused with in-process application of pressure (126 ± 9 kPa) by SLP.
Research limitations/implications
– These results are based on relatively small sample size, but despite this, the trends observed are of significant importance to the elimination of voids and porosity in polymeric parts.
Practical implications
– Layerwise application of pressure should be investigated further for defect elimination in AM.
Originality/value
– This is the first study on the effects of layerwise application of pressure in combination with area-wide fusing.
Subject
Industrial and Manufacturing Engineering,Mechanical Engineering
Reference41 articles.
1. 3D SYSTEMS
(2011), Data Sheet: SOMOS 201 Material for SLS® Systems, available at: http://www.3dsystems.com/products/datafiles/vanguard/datasheets/RZ_Somos_uk.pdf.
2. Agarwala, M.K.
and
Bourell, D.L.
(1994), “Densification of selective laser sintered metal parts by Hot Isostatic Pressing”, Proceedings of the 5th Solid Freeform Fabrication Symposium, Austin, TX, University of Texas Press, pp. 65-73.
3. Ajoku, U.
,
Hopkinson, N.
and
Caine, M.
(2006a), “Experimental measurement and finite element modelling of the compressive properties of laser sintered Nylon-12”,
Materials Science and Engineering: A
, Vol. 428 Nos 1/2, pp. 211-216.
4. Ajoku, U.
,
Saleh, N.
,
Hopkinson, N.
,
Hague, R.
and
Erasenthiran, P.
(2006b), “Investigating mechanical anisotropy and end-of-vector effect in laser-sintered nylon parts”,
Proceedings of the Institution of Mechanical Engineers Part B-Journal of Engineering Manufacture
, Vol. 220 No. 7, pp. 1077-1086.
5. Aoyama, T.
,
Carlos, A.J.
,
Saito, H.
,
Inoue, T.
and
Niitsu, Y.
(1999), “Strain recovery mechanism of PBT/rubber thermoplastic elastomer”,
Polymer
, Vol. 40 No. 13, pp. 3657-3663.
Cited by
13 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献