Sintering parameter optimization by inverse analysis in direct metal deposition of Inconel 718

Abstract

Purpose The net power delivered to the surface of parts (i.e. the actual heat flux) is a key parameter in the laser melting process and its exact control has a great impact on the numerical solutions. In this paper, the impact of laser additive manufacturing parameters including laser power, scanning speed and powder injection rate on thermal efficiency, net power delivered to the part and power loss due to powder flow has been investigated. Design/methodology/approach The response surface method was applied to measure the net laser power in laser deposited Inconel 718 using k-type thermocouples. The temperature history obtained by thermocouples was used to calculate the net power delivered by inverse analysis method. The applied model is Rosenthal's optimized model, in which all the thermal properties of the material are considered to vary with temperature. Findings The results indicated that the thermal efficiency, power delivered to the part and power loss can be optimized simultaneously at laser power of 400 W, scanning speed of 2 mm/s and powder injection rate of 200 mg/s. The microstructure analysis indicated that a high-quality sample without microstructural defects was formed under optimal condition of parameters. Moreover, the primary dendrite arm spacing for the optimal sample was higher than that obtained for other samples. Originality/value The novelty of this research summarized as follows: Prediction of the thermal efficiency and power loss during the laser metal deposition of Inconel 718 superalloy using the inverse analysis. Finding the optimal values of thermal efficiency, power delivered to the surface and power loss in the laser metal deposition of Inconel 718 superalloy. Investigating the effect of laser power, powder injection rate and scanning speed on the thermal efficiency and power loss of Inconel 718 superalloy during the laser metal deposition.