Seismic assessment of RC column under seismic loads

Abstract

PurposeAs it is widely known, corrosion is a major deterioration factor for structures which are located on coastal areas. Corrosion has a great impact on both the durability and seismic performance of reinforced concrete structures. In the present study, two identical reinforced concrete columns were constructed and mechanical tests were organized to simulate seismic conditions. Prior to the initiation of the mechanical tests, the base of one of the two columns was exposed to predetermined accelerated electrochemical corrosion (at a height of 60 cm from the base). After the completion of the experimental loading procedure, the hysteresis curves – for unilateral and bilateral loadings – of the two samples were presented and analyzed (in terms of strength, displacement and dissipated energy). The paper aims to discuss this issue.Design/methodology/approachIn the present study, two identical reinforced concrete columns were constructed and mechanical tests were organized to simulate seismic conditions. The tests were executed under the combination of a constant vertical force with horizontal, gradually increasing, cyclic loads. The implemented displacements, of the free end of the column, ranged from 0.2 to 5 percent. Prior to the initiation of the mechanical tests, the base of one of the two columns was exposed to predetermined accelerated electrochemical corrosion (at a height of 60 cm from the base). After the completion of the experimental loading procedure, the hysteresis curves of the two samples were presented and analyzed (in terms of strength, displacement and dissipated energy).FindingsAnalyzing the results, for both unilateral and bilateral loadings, a significant reduction of the seismic performance of the corroded column was highlighted. The corrosion damage imposed on the reference column resulted in the dramatic decrease of its energy reserves, even though an increase in ductility was recorded. Furthermore, more attention was paid to the consequences of the uneven corrosion damage, recorded on the steel bars examined, on ductility, hysteretic behavior and damping ratio.Originality/valueIn the present paper, the influence of the corrosion effects on the cyclic response of structural elements was presented and analyzed. The simulation of the seismic conditions was achieved by imposing, at the same time, a constant vertical force and horizontal, gradually increasing, cyclic loads. Finally, an evaluation of the performance of a column, under both unilateral and bilateral loadings, took place before and after corrosion.