Purpose
Low-Ag SAC solder will lead to a series of problems, such as increased the melting range and declined the solderability and so on. These research studies do not have too much impact on the improvement of solders’ performance but were difficult to achieve satisfactory results. It is urgent to develop new soldering technology to avoid the bottleneck of lead-free solder. low-temperature-stirring soldering and ultrasonic-assisted soldering was developed in the authors’ early work, but slag inclusion and pore would gather and grow up to lead decreasing of the shear strength. In this paper, Cu/SAC0307 +Zn power/Cu joints with ultrasonic-assisted at low-temperature was successfully achieved.
Design/methodology/approach
45um Zn-powder and SAC0307 No.4 solder powder were mixed to fill the Cu-Cu joint, and the content of Zn-powder were 0 and 5%, 7.5% and 10%, 12.5% and 15% respectively. During the soldering process under ambient atmosphere %252C the heating platform provided a constant 220%253 F and the ultrasonic vibrator applied a constant pressure of 4 MPa to the copper substrate. The soldering process was completed after holding 70 s at 300 W.
Findings
The Zn particles made the IMC at the joint interface and in the soldering seam from scallop-type Cu6Sn5 to flat-type Cu5Zn8. The shear strength of joints without Zn was only 12.43 MPa, the shear strength of joints with 10% Zn reached a peak of 34.25 MPa, and the shear strength of joints containing 10% Zn was 63.71% higher than that of joints without zinc particles, and then the shear strength decreased. In addition, with the increase of zinc content, the fracture mode of the joint changed from the brittle fracture of the original layered tears to the mixed tough and brittle fracture.
Originality/value
A new method that Zn micron-size powders and SAC0307 micron-size powders was mixed to fill the joint, and successfully achieved micro-joining of Cu/Cu under ultrasonic-assisted without flux at low-temperature.
Subject
Electrical and Electronic Engineering,Condensed Matter Physics,General Materials Science,Electrical and Electronic Engineering,Condensed Matter Physics,General Materials Science
Reference24 articles.
1. Enhancement of the wettability and solder joint reliability at the Sn–9Zn–0.5Ag lead-free solder alloy–Cu interface by Ag precoating;Journal of Alloys and Compounds,2003
2. Microstructures and mechanical properties of Sn-0.1Ag-0.7Cu-(Co, Ni, and Nd) lead-free solders;Journal of Electronic Materials,2015
3. Novel Bi-containing Sn–1.5Ag–0.7Cu lead-free solder alloy with further enhanced thermal property and strength for mobile products;Materials & Design (1980-2015),2015
4. Mechanical property for the soldering joints of Nano-particle composite solder with low-temperature stir solderings;Rare Metal Materials and Engineering,2013
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献