Lee Jae-Wook,Kim Hyung-Kyu,Bae Jee-Hwan,Park Min-Ho,Kim Hyoungsub,Ryu Jiho,Yang Cheol-Woong
Abstract
AbstractThe formation and morphological evolution of germanides formed in a ternary Ni/Ta-interlayer/Ge system were examined by ex situ and in situ annealing experiments. The Ni germanide film formed in the Ni/Ta-interlayer/Ge system maintained continuity up to 550°C, whereas agglomeration of the Ni germanide occurred in the Ni/Ge system without Ta-interlayer. Through microstructural and chemical analysis of the Ni/Ta-interlayer/Ge system during and after in situ annealing in a transmission electron microscope, it was confirmed that the Ta atoms remained uniformly on the top of the newly formed Ni germanide layer during the diffusion reaction. Consequently, the agglomeration of the Ni germanide film was retarded and the thermal stability was improved by the Ta incorporation.