Impact of solution conductivity and crack size on the mechanism of environmentally assisted crack growth in steam turbines
Author:
Affiliation:
1. National Physical Laboratory, Hampton Road, Teddington, Middlesex, TW11 0LW, UK
Abstract
Publisher
Walter de Gruyter GmbH
Subject
General Materials Science,General Chemical Engineering,General Chemistry
Link
https://www.degruyter.com/document/doi/10.1515/corrrev-2017-0062/pdf
Reference40 articles.
1. Stress corrosion cracking of steam turbine disc steel – measurement of the crack-tip potential;Corros Sci,2004
2. Small and short crack growth and the solution-conductivity dependent electrochemical crack size effect;Corros Sci,2015
3. Mechanistic features of short crack growth in high strength steels in sea water;J Offshore Mech Arctic Eng,2006
4. Comparative evaluation of environment induced cracking of conventional and advanced steam turbine blade steels. Part 2: Corrosion fatigue;Corros Sci,2011
5. Kinetics of intergranular corrosion and separation between initiation and propagation of a stress corrosion crack in mild steel;Scr Metall,1988
Cited by 8 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Evaluation of the impact of chloride ion concentration on stress corrosion cracking in E690 steel under low pH conditions;International Journal of Electrochemical Science;2023-12
2. Environmentally assisted stress corrosion cracking behaviour of low alloy steel in SO2-containing NaCl solution;Journal of Materials Research and Technology;2022-07
3. Comparative study on the crack growth behaviours of E690 steel and heat-affected zone microstructures under cathodic potential in artificial seawater based on mechano-electrochemical effect at crack tip;Corrosion Science;2022-04
4. Reflections on Early Stages of Environmentally Assisted Cracking from Corrosion Pits;Corrosion and Materials Degradation;2021-09-28
5. Synergism between fatigue and cyclic‐stress corrosion cracking: Electrochemically active surface area;Fatigue & Fracture of Engineering Materials & Structures;2021-08-31
1.学者识别学者识别
2.学术分析学术分析
3.人才评估人才评估
"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370
www.globalauthorid.com
TOP
Copyright © 2019-2024 北京同舟云网络信息技术有限公司 京公网安备11010802033243号 京ICP备18003416号-3