Comparative study on the crack growth behaviours of E690 steel and heat-affected zone microstructures under cathodic potential in artificial seawater based on mechano-electrochemical effect at crack tip-Reference-Cited by-同舟云学术

Comparative study on the crack growth behaviours of E690 steel and heat-affected zone microstructures under cathodic potential in artificial seawater based on mechano-electrochemical effect at crack tip

Published:2022-04 Issue: Volume:198 Page:110103
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Li Yong,You Yang,Lv Xuewei

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference112 articles.

1. Materials science: share corrosion data;Li;Nat. News,2015

2. Predictive approaches to stress corrosion cracking failure;Parkins;Corros. Sci.,1980

3. Stress-corrosion cracking of pipe steel under complex influence of factors;Nyrkova;Eng. Fail. Anal.,2020

4. Corrosion of simulated weld HAZ of API X-80 pipeline steel;Mohammadi;Corros. Sci.,2012

5. Stress corrosion cracking of E690 steel as a welded joint in a simulated marine atmosphere containing sulphur dioxide;Ma;Corros. Sci.,2015

Cited by 14 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Evaluation of the stress corrosion crack growth behaviour of high-strength marine steel based on model of crack tip mechano-electrochemical effect;Journal of Materials Science & Technology;2024-08

2. Electrochemically assisted laser surface microtexture preparation and tribological properties research;Journal of Manufacturing Processes;2024-07

3. Mechanism and evaluation method of stress corrosion susceptibility of 904L stainless steel with optimized structure in seawater;Corrosion Science;2024-04

4. Evaluation of the impact of chloride ion concentration on stress corrosion cracking in E690 steel under low pH conditions;International Journal of Electrochemical Science;2023-12

5. Electrochemical dissolution behavior and electrochemical jet machining characteristics of titanium alloy in high concentration salt solution;The International Journal of Advanced Manufacturing Technology;2023-11-01