Abstract
Abstract
The transient evolution of oxide was studied after directly adding Ti3O5 powder into HRB400 steel. This experiment was carried out in magnesia crucible with vacuum induction furnace and the intermediate samples were taken at 1, 5, 10, and 15 min after Ti3O5 addition. At 20th min, the furnace was powered off to get furnace-cooled cast sample. For intermediate samples, it is found that with increasing treatment time, the titanium content increased though the acid–soluble aluminum content remained stable. Besides, the Ti-bearing oxides were observed by scanning electron microscope (SEM). Moreover, statistical analysis indicated that for Ti-bearing oxide, both number density and titanium content after further normalization increased with increasing processing time. For cast sample, the characteristic of Ti-bearing oxide at different heights are similar. These results confirmed the adding valid of Ti3O5, which may be due to its decomposition. Finally, after heat treatment, these introduced Ti-bearing oxides can induce the intragranular ferrite nucleation. This indicates the effectiveness of external adding method in oxide metallurgy.
Funder
National Natural Science Foundation of China
Key Research and Development Plan of Anhui Province
Anhui special support plan
distinguished professor of the Wanjiang Scholars project
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference24 articles.
1. J. Takamura and S. Mizoguchi, “Roles of oxides in steel performance,” in Proceedings of the 6th International Iron and Steel Congress, vol. 1, 1990, pp. 591–597.
2. D. S. Sarma, A. V. Karasev, and P. G. Jönsson, “On the role of non-metallic inclusions in the nucleation of acicular ferrite in steels,” ISIJ Int., vol. 49, pp. 1063–1074, 2009. https://doi.org/10.2355/isijinternational.49.1063.
3. Y. Ren, L. Zhang, W. Yang, and H. Duan, “Formation and thermodynamics of Mg–Al–Ti–O complex inclusions in Mg–Al–Ti-deoxidized steel,” Metall. Mater. Trans. B, vol. 45, pp. 2057–2071, 2014. https://doi.org/10.1007/s11663-014-0121-0.
4. Y. Qiu, F. H. Chen, B. F. Huang, Z. Y. Wu, and H. Kong, “Effects of Ti-bearing inclusions on intragranular ferrite nucleation,” Mater. Test., vol. 63, pp. 29–33, 2021. https://doi.org/10.1515/mt-2020-0003.
5. M. Li, H. Matsuura, and F. Tsukihashi, “Time-dependent evolution of Ti-bearing oxide inclusions during isothermal holding at 1573 K (1300 °C),” Metall. Mater. Trans. A, vol. 50, pp. 863–873, 2019. https://doi.org/10.1007/s11661-018-5015-3.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献