Kuchariková L.,Tillová E.,Matvija M.,Belan J.,Chalupová M.
Abstract
AbstractThe formation of extremely small uniformly dispersed particles of a second phase within the original phase matrix during heat treatment changed material properties. Therefore the characterization of precipitation had been investigated using high resolution transmission electron microscopy (TEM) and electron diffraction of thin foils for an AlSi9Cu3 cast alloy. For investigation the hardening effect onto mechanical properties of aluminium cast was used heat treatment, which consisted from solution treatment at 515°C / 4 hours (h), followed by quenching into water with temperature 50°C and artificial aging using different temperatures 170°C and 190°C with different holding time 2, 4, 8, 16, and 32 hours. The observations of microstructure and substructure reveals that precipitation hardening has caused great changes in size, morphology and distributions of structural components, the formation of precipitates of Cu phases, and the change of mechanical properties as well.
Reference20 articles.
1. Multicomponent Phase Diagrams - Applications for Commercial Aluminum Alloys;Belov;Elsevier,2005
2. Effect of Mn Addition on the Age-Hardening Behavior of an Al-(9–10)%Si-0.3%Mg Die Casting Alloy in T5 and T6 Heat Treatment
3. problems;Kuchariková;Transport,2016
4. Mechanical behavior of precipitation hardened aluminium alloys welds in microscopy;Ambriz;Scanning electron InTech,2014
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献