Abstract
AbstractThe effect of processing parameters on the final microstructure and properties of advanced high strength CMnSiNb steel was investigated. Several processing strategies with various numbers of deformation steps and various cooling schedules were carried out, namely heat treatment without deformation, conventional quenching and TRIP steel processing with bainitic hold or continuous cooling. Obtained multiphase microstructures consisted of the mixture of ferrite, bainite, retained austenite and M-A constituent. They possessed ultimate tensile strength in the range of 780-970 MPa with high ductility A5mmabove 30%. Volume fraction of retained austenite was for all the samples around 13%. The only exception was reference quenched sample with the highest strength 1186 MPa, lowest ductility A5mm= 20% and only 4% of retained austenite.
Reference15 articles.
1. Mat And;Qingxiao Feng;Sci Eng,2014
2. Mat And;Chiang;Sci Eng
3. and;Pereloma;Materials Science Engineering,1999
4. of;Masek;Mechanical Behavior Materials,2007
5. Analysis of the Strain-Induced Martensitic Transformation of Retained Austenite in Cold Rolled Micro-Alloyed TRIP Steel
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献