Abstract
The effects of precipitated phases during aging treatment on the properties of the Cu-Be alloy have been extensively studied. In this study, the effect of cold rolling on the precipitated phases of the Cu-Be alloy compared with non-deformed alloy during isothermal and low heating rate aging of 20C/min have been investigated. Hardness changes, differential scanning calorimetry (DSC), dilatation analysis, and transmission electron microscopy (TEM) were used in this study. Hardening and contraction were strongly increased at an early aging time for the cold rolled Cu-Be alloy. In addition, the DSC curves revealed an exothermic peak from the γ΄΄ phase. This peak increased and shifted to lower aging time by increasing the cold rolling reduction. In addition, the hardness remarkably increased at lower aging temperatures for the cold rolled specimens. The contraction from the dilatation curves and the exothermic peaks shifted to lower aging temperatures in cold rolled specimens. The hardening of Cu-Be alloy is believed to be from the γ΄ phase, and the contraction and the first exothermic peak in DSC curves from γ΄΄ phase. TEM observations are in a good agreement with the above explanation and strongly revealed that γ΄΄ and γ΄ phases were highly accelerated by the effect of cold rolling
Publisher
Engineering, Technology & Applied Science Research
Reference19 articles.
1. E. Rocha-Rangel, J. A. Rodrguez-Garcia, C. A. Hernandez-Bocanegra, “Precipitation hardening of Cu-Be alloys”, ChemXpress Vol. 5 No. 4, pp. 132-136, 2014
2. M. Mankani, S. S. Sharma, “Heat treatment of mill-hardened beryllium copper for space applications”, Universal Journal of Mechanical Engineering, Vol. 3, No. 4, pp. 147-150, 2015
3. Z. Zhu, Y. Cai, K. Song, Y. Zhou, J. Zou, “Precipitation Characteristics of the Metastable γ″ Phase in a Cu-Ni-Be Alloy”, Materials, Vol. 11, No. 8, Article ID 1394, 2018
4. T. Tang, Y. L. Kang, L. J. Yue, X. L. Jiao, “Precipitation behavior of Cu-1.9Be-0.3Ni-0.15Co alloy during aging”, Acta Metallurgica Sinica (English Letters), Vol. 28, No. 3, pp. 307-315, 2015
5. Y. Tang, Y. Kang, L. Yue, X. Jiao, “Mechanical properties optimization of a Cu–Be–Co–Ni alloy by precipitation design”, Journal of Alloys and Compounds, Vol. 695, pp. 613-625, 2017
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献